Photo Electrochemical Study on Brush Electrodeposited CuGaS2 Thin Films |
|
|
|
PP: 27-31 |
|
|
|
doi:10.18576/ijtfst/140105
|
|
|
|
Author(s) |
|
|
|
B. Kajamaideen,
A. Basker,
KR. Murali,
|
|
|
|
Abstract |
|
|
| For the first time copper gallium sulphide (CuGaS2) films were prepared using the brush plating method at various electrolyte temperatures between 30 and 80 degrees Celsius with a steady current density of 5.0mA cm-2 CuGaS2 photo electrodes that were coated at 80 degrees Celsius and then post-heated at various temperatures with Intensity -
60 mW cm-2. CuGaS2 film electrode that was coated at a temperature of 80 degrees Celsius and post-heated at 525°C lead to variation in photocurrent with wavelength. CuGaS2 films coated at temperatures ranging from 30°C to 80°C displays photocurrent - characteristic curve. CuGaS2 photo electrode Mott Schottky graph with electrolyte temperature of 80°C and post-heat processing of 525°C.
|
|
|
|
|
|
|
|